Etching method and etching device

ABSTRACT

Disclosed is a dry etching method for etching a metal film on a substrate with the use of an etching gas, wherein the etching gas contains a β-diketone and first and second additive gases; wherein the metal film contains a metal element capable of forming a complex with the β-diketone; wherein the first additive gas is at least one kind of gas selected from the group consisting of NO, NO 2 , O 2  and O 3 ; wherein the second additive gas is at least one kind of gas selected from the group consisting of H 2 O and H 2 O 2 ; wherein the amount of the β-diketone contained is 10 vol % to 90 vol % relative to the etching gas; and wherein the amount of the second additive gas contained is 0.1 vol % to 15 vol % relative to the etching gas. The etching rate of the metal film is increased by this etching method.

FIELD OF THE INVENTION

The present invention relates to a technique for etching a metal film with the use of an etching gas containing a β-diketone.

BACKGROUND ART

The manufacturing process of semiconductor devices sometimes includes etching metal films formed on substrates to be used as wiring materials, metal gate materials, electrode materials or magnetic materials.

With the fine processing of semiconductor devices, there has been a demand to highly control the etching of metal films for the purpose of etching the metal films into a fine structures. More specifically, researches have been made to etch the metal film with etching depth variations of 1 nm or less in the wafer plane, to control the surface roughness of the metal film after the etching, to selectively etch the metal film, and the like. It is however difficult to perform such high etching control by a wet etching method in which a metal film is etched with a chemical solution. A dry etching method in which a metal film is etched with a gas is being studied for high etching control.

For example, Patent Document 1 discloses an etching method which includes an etching step of etching a thin film on a substrate with an etching gas containing a β-diketone with at least one of water and alcohol, under a condition that the temperature of the substrate is 300° C. or higher, preferably 450° C. or higher, thereby exposing a surface of the substrate. Further, Patent Document 2 discloses an etching method for etching a metal film by using an etching gas containing a β-diketone and 1 to 20 vol % of water or hydrogen peroxide and forming a complex of the β-diketone and the metal element of the metal film in a temperature range of 100° C. to 350° C. In Patent Document 2, zinc, cobalt, hafnium, iron, manganese, vanadium and the like are described as examples of the metal element of the metal film. It is reported in Patent Document 2 that the etching rate of the metal film becomes higher with the addition of water or hydrogen peroxide than with the use of oxygen.

The use of β-diketones has also been proposed, not for fine etching of metal films formed on substrates, but for dry cleaning of metal films deposited in film-forming apparatuses in semiconductor manufacturing process.

For example, Patent Document 3 discloses a dry cleaning method for removing a metal film deposited in a film-forming apparatus by reacting the metal film with a cleaning gas containing a β-diketone and NOx (either one of NO and N₂O) in a temperature range of 200 to 400° C., preferably 250 to 370° C. In Patent Document 3, nickel, manganese, iron, cobalt and the like are described as examples of the constituent metal element of the metal film in Patent Document 3. It is reported in Patent Document 3 that the temperature range in which the metal film can be etched and removed becomes wider with the use of NOx than with the use of oxygen.

PRIOR ART DOCUMENTS Patent Documents

-   Patent Document 1: Japanese Laid-Open Patent Publication No.     2004-91829 -   Patent Document 2: Japanese Laid-Open Patent Publication No.     2014-236096 -   Patent Document 3: Japanese Laid-Open Patent Publication No.     2013-194307

SUMMARY OF THE INVENTION Problems to be Solved by the Invention

It is conceivable that the cleaning gas of Patent Document 3, which contains a β-diketone and NOx (either one of NO and N₂O), could be used as an etching gas for etching a metal film. It has however been found as a result of researches made by the present inventors that, in the case of etching a metal film on a substrate by supplying a β-diketone to the substrate, there is a problem of decomposition of the β-diketone under the catalytic action of the metal whereby a film predominantly composed of carbon (hereinafter referred to as “carbon film”) remains on the substrate after the etching, or a problem of damage to the structure of a semiconductor device as the workpiece. It has also been found by the present inventors that, in the case of using NOx gas as an additive gas, it is possible to suppress the formation of a carbon film and the occurrence of damage to the workpiece by decreasing the temperature of the substrate during the etching. In such a case, however, there is a problem that the etching rate of the metal film is decreased with decrease in substrate temperature.

The present invention has been made in view of the above circumstances. It is an object of the present invention to provide a method for etching a metal film at an improved etching rate.

Means for Solving the Problems

The present inventors have found that, in the case of etching a metal film with the use of a β-diketone, the etching rate of the metal film is increased with the addition of not only an oxidizing gas such as NO but also water etc. to the β-diketone. The present invention is based on this finding.

According to one aspect of the present invention, there is provided a dry etching method comprising etching a metal film on a substrate by bringing an etching gas into contact with the metal film in a temperature range of 100° C. to 350° C., wherein the etching gas contains a β-diketone, a first additive gas and a second additive gas; wherein the metal film contains a metal capable of forming a complex with the β-diketone; wherein the first additive gas is at least one kind of gas selected from the group consisting of NO, NO₂, O₂ and O₃; wherein the second additive gas is at least one kind of gas selected from the group consisting of H₂O and H₂O₂; wherein the amount of the β-diketone contained in the etching gas is 10 vol % to 90 vol % relative to the total amount of the etching gas; and wherein the amount of the second additive gas contained in the etching gas is 0.1 vol % to 15 vol % relative to the total amount of the etching gas.

It is possible by the etching method according to the present invention to increase the etching rate of the metal film.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view of an etching device according to one embodiment of the present invention.

FIG. 2 is a schematic cross-sectional view of a filled container according to one embodiment of the present invention.

FIG. 3 is a graph showing the relationship between the amount of water in the etching gas and the rate of etching by the etching gas in Example and Comparative Example.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Hereinafter, embodiments of the present invention will be described in detail below. It should be understood that: the present invention is not limited to the following embodiments; and various changes and modifications of the following embodiments can be made as appropriate without departing from the scope of the present invention.

(Etching Method of Metal Film)

One embodiment of the present invention is a dry etching method for etching a metal film on a substrate with the use of an etching gas, wherein the etching gas contains a β-diketone, a first additive gas and a second additive gas; and wherein the metal film contains a metal element capable of forming a complex with the β-diketone.

When the etching gas is introduced into an etching device in which the workpiece with the metal film is placed, and then, brought into contact with the metal film of the workpiece under heating, a metal complex is formed by reaction of the β-diketone with the metal element of the metal film. Since the metal complex is high in vapor pressure, the metal film is removed by vaporization of the metal complex. The present invention is characterized in that the etching rate of the metal film is increased with the addition of the first and second additive gas into the etching gas.

It is assumed that, in the present invention, the etching rate is increased because: the first additive gas added has oxidizing ability and thus can oxide the metal film; and the second additive gas added can form the metal complex by being bonded to the β-diketone and to the metal element of the metal film.

In the present invention, the etching rate is determined as the amount of decrease of the thickness of the metal film per unit time (in units of nm/min) based on a difference in weight (i.e. weight change) of the workpiece before and after etching treatment and a specific gravity of the metal film.

The metal film, as the etching target to be processed by the dry etching method in the present invention, contains a metal element capable of forming a complex with the β-diketone as mentioned above. The metal element can be at least one kind of element selected from the group consisting of Co, Fe, Ni, Zn, Hf, V and Cu. The metal film can be a film composed of only one of the above-mentioned elements or can be a film composed of two or more elements including any of the above-mentioned elements. Examples of the metal film are those made of metal compounds, such as NiSi, CoSi, HfSi, NiCo, FeCo, CoPt, MnZn, NiZn, CuZn and FeNi, and oxides thereof. The present invention is particularly effective for etching of the metal film containing Co. In the present invention, the substrate can be a known semiconductor substrate, glass substrate or the like.

The first additive gas is at least one kind of gas selected from the group consisting of NO, NO₂, O₂ and O₃. The second additive gas is at least one kind of gas selected from the group consisting of H₂O and H₂O₂.

Examples of the β-diketone usable in the present invention are hexafluoroacetylacetone, trifluoroacetylacetone and acetylacetone. The β-diketone can be of one kind or of two or more kinds in combination. For high-rate etching, hexafluoroacetylacetone and trifluoroacetylacetone are preferred. The etching rate of the metal film is increased with increase in the concentration of the β-diketone contained in the etching gas. In the case where the vapor pressure of the β-diketone is so low that there is a possibility of liquefaction of the β-diketone in a film forming apparatus, however, it is preferable to adjust the concentration of the β-diketone in the etching gas with the addition of a diluent gas.

From the viewpoint of attaining a sufficient etching rate, the amount of the β-diketone contained in the etching gas is preferably 10 vol % to 90 vol %, more preferably 30 vol % to 60%, relative to the etching gas composition.

From the viewpoint of attaining a sufficient etching rate, the amount of the first additive gas contained in the etching gas is preferably 0.01 vol % to 10 vol %, more preferably 0.05 vol % to 8 vol %, still more preferably 0.1 vol % to 5 vol %, relative to the etching gas composition.

Further, the amount of the second additive gas contained in the etching gas is generally 0.1 vol % to 15 vol %, preferably 0.5 vol % to 10 vol %, more preferably 2 vol % to 8 vol %, relative to the etching gas composition. The content rate of the second additive gas to the β-diketone in the etching rate is preferably 0.5 vol % to 50 vol %, more preferably 1 vol % to 20 vol %.

The etching gas may contain an inert gas such as N₂, He, Ar, Ne, Kr or the like in addition to the β-diketone and the first and second additive gases. As long as the etching gas is diluted to an appropriate concentration with the addition of the inert gas, there is no particular limitation on the amount of the inert gas contained in the etching gas. The amount of the inert gas contained in the etching gas is generally 1 vol % to 90 vol %, preferably 10 vol % to 80 vol %, more preferably 30 vol % to 50 vol %, relative to the etching gas composition.

(Etching Device)

The dry etching method according to the present invention can be embodied in an ordinary etching device for semiconductor manufacturing process as shown in FIG. 1. More specifically, one embodiment of the present invention is an etching device 100 including: a treatment chamber 110 in which the substrate (as a workpiece 112) with the metal film containing a metal element capable of forming a complex with the β-diketone is placed; a β-diketone supply unit 130 connected to the treatment chamber 110 and configured to supply the β-diketone; a first additive gas supply unit 140 connected to the treatment chamber 110 and configured to supply the first additive gas; a second additive gas supply unit 150 connected to the treatment chamber 110 and configured to supply the second additive gas; an inert gas supply unit 160 connected to the treatment chamber 110 and configured to supply the inert gas; a heating unit 170 configured to heat the treatment chamber 110; and a control unit (not shown) connected to the β-diketone supply unit 130, the first additive gas supply unit 140, the second additive gas supply unit 150 and the like and configured to output control signals to control valves 135, 145, 155 and 165 to supply the β-diketone and the other gases to the workpiece 112.

The treatment chamber 110 includes therein a placement stage 111 on which the workpiece 112 is placed. There is no particular limitation on the treatment chamber 110 as long as the treatment chamber 110 is resistant to the β-diketone used and is capable of being evacuated to a predetermined pressure level. In general, an ordinary treatment chamber of a semiconductor etching device can be utilized as the treatment chamber 110. There is also no particular limitation on the pipes 121, 131, 141, 151 and 161 for supply of the etching gas and the other pipes 171 a and 171 b as long as these pipes are resistant to the β-diketone used. Ordinary pipes can be utilized.

The β-diketone supply unit 130 is connected to the treatment chamber 110. The β-diketone is supplied from the β-diketone supply unit 130 into the treatment chamber 110 through the pipe 121. As shown in FIG. 1, the β-diketone supply unit 130 is equipped with a valve 135 and a flow rate regulator 133 so as to regulate the amount of the β-diketone supplied. The regulated amount of the β-diketone is fed from the pipe 131 to into the pipe 121. Further, the inert gas supply unit 160 is equipped with a valve 165 and a flow rate regulator 163 so as to regulate the amount of the inert gas supplied as the diluent gas. The regulated amount of the inert gas is fed from the pipe 161 into the pipe 121. The first additive gas supply unit 140 is equipped with a valve 145 and a flow rate regulator 143 so as to regulate the amount of the first additive gas supplied. The regulated amount of the first additive gas is fed from the pipe 141 into the pipe 121. The second additive gas supply unit 150 is equipped with a valve 155 and a flow rate regulator 153 to regulate the amount of the second additive gas supplied. The regulated amount of the second additive gas is fed from the pipe 151 into the pipe 121.

It is preferable in the etching device 100 that the β-diketone is supplied in a state of being diluted to a predetermined concentration with the inert gas supplied from the inert gas supply unit 160 and being mixed at a predetermined concentration with the first and second additive gases supplied from the first and second additive gas supply units 140 and 150. The β-diketone may however not necessarily be diluted with the inert gas.

The heating unit 170 is disposed externally of the treatment chamber 110 so as to heat the treatment chamber 110. As a second heating unit, a heater (not shown) may be disposed inside the placement stage 111. In the case where the treatment chamber 110 has a plurality of placement stages, heaters may be provided in the respective placement stages so as to individually set the temperatures of the placement stages to predetermined degrees.

A gas discharge unit for discharge of the gas after the reaction is disposed on one side of the treatment chamber 110. The discharge gas unit has a vacuum pump 173 by which the gas after the reaction is discharged from the treatment chamber 110 through the pipe 171 a. The gas after the reaction is collected in a liquid nitrogen trap 175 which is disposed between the pipes 171 a and 171 b. Valves 177 a and 177 b are disposed between the pipes 171 a and 171 b so as to regulate the pressure of the gas. In FIG. 1, PI 123 and PI 125 are pressure gauges. Base on the readings of these pressure gauges, the respective flow rate regulators and valves are controlled by the control unit.

An implementation example of the etching method by the etching device 100 will be now explained below.

The substrate (workpiece 112) with the metal film containing a metal element capable of forming a complex with the β-diketone is placed in position. The insides of the treatment chamber 110, the pipes 121, 131, 141, 151 and 161, the liquid nitrogen trap 175 and the pipes 171 a and 171 b are evacuated to a predetermined pressure level by the vacuum pump 173. After that, the workpiece 112 is heated by the heating unit 170. When the temperature of the workpiece 112 reaches a predetermined degree, the β-diketone, the first and second additive gases and the diluent gas are respectively supplied at predetermined flow rates from the β-diketone supply unit 130, the first and second additive gas supply units 140 and 150 and the inert gas supply unit 160 into the pipe 121.

The β-diketone is diluted and then mixed at a predetermined composition ratio with the additive gases. The thus-mixed etching gas is supplied into the treatment chamber 110. While introducing the mixed etching gas into the treatment chamber 110, the pressure inside treatment chamber 110 is controlled to a predetermined pressure level. Then, the metal film is subjected to etching treatment by reacting the metal film with the etching gas for a predetermined time. In the present invention, the etching treatment enables plasmaless etching. There is thus no need to excite the etching gas into a plasma during the etching treatment.

After the completion of the etching treatment, the heating operation of the heating unit 170 is stopped so that the workpiece is cooled; and the evacuating operation of the vacuum pump 173 is stopped so that the vacuum inside the treatment chamber and the like is released. As explained above, the metal film is etched by the etching method according to the present invention.

(Etching Conditions)

In the etching method according to the present invention, the etching treatment is performed at any temperature where the complex can be vaporized. In particular, the temperature of the etching target metal film during the etching treatment is preferably in a range of 100° C. to 350° C., more preferably higher than or equal to 150° C. and lower than 250° C. There is no particular limitation on the pressure inside the treatment chamber during the etching treatment. The pressure inside the treatment chamber during the etching treatment is generally in a range of 0.1 kPa to 101.3 kPa.

In the case where: the etching target metal film contains cobalt; and the etching gas contains hexafluoroacetylacetone as the β-diketone and nitrogen monoxide as the additive gas, the etching of the metal film by the etching gas at a high temperature of about 300 to 400° C. may result in a problem of carbon film formation by decomposition of the hexafluoroacetylacetone or a problem of damage to the device structure. In view of these problems, it is preferable that the workpiece is heated at a temperature higher than or equal to 150° C. and lower than 250° C., more preferably higher than or equal to 200° C. and lower than 250° C., still more preferably higher than or equal to 220° C. and lower than 250° C. In the above temperature range, the pressure inside the treatment chamber is preferably set to 20 Torr to 300 Torr (2.67 kPa to 39.9 kPa), more preferably 50 Torr to 250 Torr (6.67 kPa to 33.3 kPa), still more preferably 100 Torr to 200 Torr (13.3 kPa to 26.7 kPa), from the viewpoint of attaining a sufficient etching rate.

There is no particular limitation on the etching time. In view of the efficiency of the semiconductor manufacturing process, the etching time is preferably 60 minutes or less. Herein, the etching time refers to a time elapsed from the introduction of the etching gas into the treatment chamber in which the substrate is placed and subjected to etching treatment until the discharge of the etching gas from the treatment chamber by the vacuum pump etc. for completion of the etching treatment.

(Pretreatment of Workpiece)

Pretreatment may be performed on the workpiece as required. In the case where the etching target metal film contains cobalt, for example, etching rate variations depending on the thickness of the metal film are improved by reducing natural cobalt oxide.

It is feasible to perform the pretreatment by e.g. supplying a reducing gas to the workpiece 112 from a reducing gas supply unit (not shown).

In this reducing gas supply step, the reducing gas supplied can be, but is not limited to, hydrogen gas. Gas of carbon monoxide (CO), formaldehyde (HCHO) or the like can also be used as the reducing gas.

Although the reducing gas such as hydrogen gas can be supplied solely in the reducing gas supply step, it is preferable to dilute the reducing gas with a diluent gas such as nitrogen gas.

It is further preferable that the β-diketone and nitrogen monoxide gas are not supplied in the reducing gas supply step. More specifically, the amount of the β-diketone and nitrogen monoxide gas supplied is preferably less than 0.01 vol %, more preferably less than 0.001 vol %, still more preferably 0 vol %, relative to the total amount of the gases supplied in the reducing gas supply step.

There is no particular limitation on the treatment temperature of the reducing gas supply step as long as the treatment temperature is in the range where the natural oxide can be reduced. When the treatment temperature of the reducing gas supply step is low, however, the reduction reaction of the natural oxide does not almost proceed. Although the treatment temperature of the reducing gas supply step can be set high, the treatment temperature of the reducing gas supply step is preferably equal to the treatment temperature of the first mixed gas supply step from the viewpoint of operation of the etching device. It is consequently preferable in the reducing gas supply step that the workpiece is heated to 100° C. to 350° C., more preferably 150° C. to 250° C., still more preferably 200° C. to 250° C.

In the reducing gas supply step, the flow rate of the reducing gas is varied depending on the volume of the treatment chamber. There is no particular limitation on the pressure inside the treatment chamber during the reducing gas supply step. The pressure inside the treatment chamber during the reducing gas supply step is set appropriately within the range of e.g. 10 to 500 Torr (1.33 to 66.5 kPa) according to the device.

The treatment time of the reducing gas supply step can be adjusted as appropriate depending on the film forming method of the metal film on the substrate and the like.

(Filled Container)

In the present invention, the β-diketone supply unit 130 can be a β-diketone filled container 200 having a sealed container body 201 filled with a β-diketone as shown in FIG. 2. The β-diketone filled container 200 is obtained by charging the β-diketone in liquid form into the sealed container body 201. In the sealed container body 201, the β-diketone is separated into a liquid phase 213 and a vapor phase 211. An outlet port 203 for charging and discharging of the β-diketone is attached to the sealed container body 201 so that the β-diketone in the vapor phase 211 can be supplied in gaseous form from the outlet port. In the case of supplying the β-diketone in gaseous form from the β-diketone filled container 200, it is necessary to heat the β-diketone filled container 200 and compensate for vaporization heat of the β-diketone in the liquid phase 213.

The β-diketone content (purity) of the β-diketone filled in liquid form into the sealed container body 201 is preferably 99 mass % or higher, more preferably 99.5 mass % or higher, still more preferably 99.9 mass % or higher. Herein, the β-diketone content (purity) of the β-diketone in liquid form is measured by gas chromatography.

(Semiconductor Device)

The etching method according to the present invention is applicable as an etching method for forming a predetermined pattern on a metal film of a conventional semiconductor device. The semiconductor device can be manufactured at low cost with the use of the metal film etched by the etching method according to the present invention. Examples of such a semiconductor device are solar cells, hard disk drives, dynamic random access memories, phase-change memories, ferroelectric random access memories, magnetoresistive random access memories, resistive random access memories, MEMS and the like.

EXAMPLES

The embodiments of the present invention will be described in more detail below by way of the following examples. It should be understood that the present invention is not limited to the following examples. The etching test of metal films was carried out as follows to examine the relationship between the amount of water contained in the etching gas and the etching rate of the metal film by the etching gas.

A β-diketone filled container was obtained by filling a sealed container body with liquid hexafluoroacetylacetone (HFAc). The hexafluoroacetylacetone used had a purity of 99.9 mass % or higher.

The etching device used was of the same type as the etching device 100 shown in FIG. 1. As the workpiece 112, a foil of cobalt (with a size of 2 cm×2 cm and a thickness of 0.1 mm) was used. The above-obtained β-diketone filled container was used as the β-diketone supply unit.

The insides of the treatment chamber 110, the pipes 121, 131, 141, 151 and 161, the liquid nitrogen trap 175 and the pipes 171 a and 171 b were evacuated to a pressure of lower than 10 Pa. The workpiece on the placement stage 111 was heated by the heating unit 170 and the heater inside the placement stage 111. Herein, the weight of the workpiece had previously been measured. Upon confirming that the heating unit 170 and the heater inside the placement stage 111 reached 220° C., the reducing gas supply step was performed as the pretreatment by supplying hydrogen gas at a rate of 10 sccm and a pressure of 50 Torr from a hydrogen gas supply unit for 5 minutes. After the completion of the pretreatment, the insides of the treatment chamber and the like were again evacuated to a pressure of lower than 10 Pa. Then, the β-diketone, the first and second additive gases and the inert gas were fed at predetermined flow rates into the pipe 121 so as to thereby introduce the etching gas into the treatment chamber 110 while controlling the pressure inside the treatment chamber 110 to a predetermined pressure level. After the lapse of a predetermined time from the initiation of the introduction of the etching gas, the introduction of the etching gas was stopped; and the vacuum inside the treatment chamber was released. The workpiece was taken out from the treatment chamber. The weight of the workpiece was measured. The etching rate of the metal film was determined from the amount of decrease of the thickness of the metal film based on a change in the weight of the workpiece before and after the test operation as well as the etching time.

In the etching test, the temperature of the workpiece was 220° C.; the total amount of the etching gas introduced was 100 sccm; the first additive gas used was NO; the second additive gas used was H₂O; the diluent gas used was N₂; the pressure inside the treatment chamber was 100 Torr; and the etching time was 2.5 minutes.

The etching conditions and etching rates of the respective examples and comparative example are shown in TABLE 1. Further, the relationship between the amount of water contained in the etching gas and the etching rate of the metal film by the etching gas is shown in FIG. 3.

TABLE 1 First Second additive additive Diluent β-Diketone gas gas gas Water Flow Flow Flow Flow content Etching Target rate rate rate rate amount rate [nm/ metal Kind [sccm] Kind [sccm] Kind [sccm] Kind [sccm] [vol %] min] Example 1 Co HFAc 50 NO 1 H₂O 0.5 N₂ 48.5 0.5 21 Example 2 Co HFAc 50 NO 1 H₂O 1 N₂ 48 1 24 Example 3 Co HFAc 50 NO 1 H₂O 2 N₂ 47 2 38 Example 4 Co HFAc 50 NO 1 H₂O 5 N₂ 44 5 41 Example 5 Co HFAc 50 NO 1 H₂O 8 N₂ 41 8 31 Example 6 Co HFAc 50 NO 1 H₂O 10 N₂ 39 10 22 Comparative Co HFAc 50 NO 1 H₂O 0 N₂ 49 0 12 Example 1

As is apparent from FIG. 3, the etching rate was 21 nm/min or higher in Examples 1 to 6 in which the second additive gas was contained in the etching gas, and was twice or more higher in Examples 1 to 6 than in Comparative Example 1 in which no second additive gas was contained in the etching gas. The etching rate was particularly high in Examples 3 to 5 in which the amount of water contained in the etching gas was 2 to 8 vol %. In each of the examples and comparative example, the formation of a carbon film was not observed because the temperature of the workpiece was at a low degree of 220° C.

DESCRIPTION OF REFERENCE NUMERALS

-   100: Etching device -   110: Treatment chamber -   111: Placement stage -   112: Workpiece -   121: Pipe -   130: β-Diketone supply unit -   131: Pipe -   133 Flow rate regulator -   135: Valve -   140: First additive gas supply unit -   141: Pipe -   143: Flow rate regulator -   145: Valve -   150: Second additive gas supply unit -   151: Pipe -   153: Flow rate regulator -   155: Valve -   160: Inert gas supply unit -   161: Pipe -   163: Flow rate regulator -   165: Valve -   170: Heating unit -   171 a, 171 b: Pipe -   173: Vacuum pump -   175: Liquid nitrogen trap -   177 a, 177 b: Valve -   200: β-Diketone filled container -   201: Sealed container body -   203: Outlet port -   211: Vapor phase -   213: Liquid phase 

The invention claimed is:
 1. A dry etching method comprising etching a metal film on a substrate by bringing an etching gas into contact with the metal film, wherein the etching gas contains hexafluoroacetylacetone as a β-diketone, NO as a first additive gas and H₂O as a second additive gas, wherein the metal film contains cobalt as a metal element capable of forming a complex with the β-diketone, wherein the amount of the β-diketone contained in the etching gas is 30 vol% to 60 vol% relative to the total amount of the etching gas, and wherein the amount of the second additive gas contained in the etching gas is 0.5 vol% to 10 vol% relative to the total amount of the etching gas, and wherein the etching gas is brought into contact with the metal film in a temperature range of 150° C. to 250° C.
 2. The dry etching method according to claim 1, wherein the amount of the second additive gas contained in the etching gas is 2 vol% to 8 vol% relative to the total amount of the etching gas.
 3. The dry etching method according to claim 1, wherein the amount of the second additive gas contained in the etching gas is 0.5 vol% to 50 vol% relative to the amount of the β-diketone contained in the etching gas.
 4. The dry etching method according to claim 1, wherein the first additive gas is contained in the etching gas in an amount of 0.01 vol% to 10 vol% relative to the total amount of the etching gas.
 5. The dry etching method according to claim 1, wherein the etching gas further contains at least one kind of inert gas selected from the group consisting of N₂, Ar, He, Ne and Kr.
 6. The dry etching method according to claim 1, comprising, before the etching, pretreating the metal film on the substrate by supplying a reducing gas.
 7. A manufacturing method of a semiconductor device, comprising etching a metal film on a substrate by the dry etching method according to claim
 1. 